Karakterisasi Laju Korosi Baja ST 40 Berlapis Polyester Putty Dalam Lingkungan Air Payau

Muhammad Jamaluddin Anwar, Edi Widodo

Abstract


The attack caused damage of corrosion (rust) is the general problem that causes the degradation of the material as the interaction with the environment and shorten the lifetime of material. Steel ST 40 is a common material used in the industrial, shipping, engineering products, home wares and others. Prevent the occurrence of direct contact with the outside environment by using a coating of polyester putty, serves to prevent the occurrence of oxidation reactions of the nature of corrosion. Coating using polyester putty give influence on the material test of resistance to corrosion. The missing mass on the specimen using a coating of polyester putty of mass loss reached 2,090 mg. whereas in the specimen undergoes the smallest mass loss of 1,090 mg. Whereas in the material without upholstery polyester putty of mass lost most of the specimens that do not use coating polyester putty with the missing mass reach 4,390 mg. Whereas in the specimen menggalami the smallest mass loss of 3,560 mg. On the specimen that is experiencing the highest rate of corrosion occurred in unpublished material using polyester putty of 26.11 Mpy whereas the smallest lajukorosi reached 21.52 Mpy. While the biggest missing mass on a material without polyester putty of 0.98 Mpy, the rate of corrosion of the smallest reach 0.56 Mpy.


Keywords


Corrosion rate; Brackish water environment with Polyester Putty coating

Full Text:

PDF

Article Metrics

Abstract view : 37 times
PDF - 17 times

References


[1] L. Air, L. Terhadap, And P. Berat, “Pengaruh Laju Korosi Pelat Baja Lunak Pada Lingkungan Air Laut Terhadap Perubahan Berat.,” Progr. Diploma III Tek. Perkapala, Fak. Tek. Univ. Diponegoro, Pp. 32–36, 2003.

[2] L. K. Dewi, “Studi Awal Reverse Osmosis Tekanan Rendah Untuk Air,” Pp. 1–14, 1812.

[3] J. T. Kimia And P. N. Lhokseumawe, “Untuk Aplikasi Industri Otomotif Dan Elektronik.”

[4] S. Dari, L. Lapindo, And P. Baja, “Pencegahan Korosi Dengan Menggunakan Inhibitor Natrium Silikat(Na 2 Sio 3 ) Hasil Sintesis Dari Lumpur Lapindo Pada Baja Tulangan Beton,” Dimas Happy Setyawan, Doty Dewi Risanti, Lizda Johar Mawarani. Jur. Tek. Fis. Fak. Teknol. Ind. Inst. Teknol. Sepuluh Nop. Jl. Arief Rahman Hakim, Surabaya 6011, Pp. 1–6, 2014.

[5] B. A. Pribadi, S. Uprapto, And D. W. I. Priyantoro, “Pengerasan Permukaan Baja St 40 Dengan Metode Carburizing Plasma Lucutan Pijar,” Pp. 25–26, 2008.

[6] A. P. Bayuseno, “Analisa Laju Korosi Pada Baja Untuk Material Kapal Dengan Dan Tanpa Perlindungan Cat,” Vol. 11, No. Ii, Pp. 32–37, 2009.

[7] P. Harmi Tjahjanti, E. Panunggal, And W. Harso Nugroho, “Analisa Pengaruh Bentuk Penampang Riser Terhadap Cacat Porositas,” J. Tek. Mesin, Vol. 15, No. 1, Pp. 43–49, 2014.

[8] J. Leonard, J. T. Mesin, F. Teknik, And U. Hasanuddin, “Analisis Perubahan Laju Korosi Dan Kekerasan Pada Pipa Baja Astm A53 Akibat Tegangan Dalam Dengan Metode C Ring,” Pp. 145–148, 2007.

[9] E. Widodo And S. R. Yulianto, “Optimization Of Temperature Nickel Chrome Coating To Get Best Quality Of Hardness And Thickness Of Steel St 40,” Proceeding Int. Conf. Green Technol., Pp. 88–90, 2014.

[10] V. Malau, “Pengaruh Variasi Waktu Dan Konsentrasi Larutan Nacl Terhadap Kekerasan Dan Laju Korosi Dari Lapisan Nikel Elektroplating Pada Permukaan Baja Karbon Sedang,” Pp. 147–152, 2011.

[11] P. H. Tjahjanti And H. Bramantyo, “Analysis Of Corrosion Penetration Rate (Cpr) Of Exhaust Ford Laser Assembled In 1997 Which Was Coated With Chrome (Cr),” Aip Conf. Proc., Vol. 1555, No. 1, Pp. 44–47, 2013.

[12] E. Widodo, “Analisa Laju Pelapisan Chromming Terhadap Corrosion Rate Baja St 40,” R.E.M. (Rekayasa, Energi, Manufaktur), Vol. 1, No. 2, Pp. 15–20, 2017.


Refbacks

  • There are currently no refbacks.


Copyright (c) 2017 R.E.M. (Rekayasa Energi Manufaktur) Jurnal

Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.

R.E.M (Rekyasa Energi Manufaktur) Jurnal is indexed by :

width=

Full Indexed Service.

R.E.M (Rekyasa Energi Manufaktur) Jurnal Official Partner:

Crossref logo

All article get this benefits:

  • Having DOI (Digital Object Identifier) from Crossref;
  • Preserved in LOCKSS, based at Stanford University Libraries, United Kingdom, through PKP Private LOCKSS Network program Link 1, Link 2; and
  • Indexed in several indexing services.