Pengaruh Variasi Holding Time Peleburan terhadap Karakteristik Logam Al-Si Menggunakan Cetakan Pasir

DOI: https://doi.org/10.21070/r.e.m.v3i1.1590

Author (s)


(1)  Muhammad Taufiq   (Mechanical Engineering, Universitas Muhammadiyah Malang)  
        Indonesia
(2) * Murjito Murjito   (Mechanical Engineering, Universitas Muhammadiyah Malang)  
        Indonesia
(3)  Dini Kurniawati   (Mechanical Engineering, Universitas Muhammadiyah Malang)  
        Indonesia
(*) Corresponding Author

Abstract


Molten metal is a method to form metal to be base material of making equipment and give great advantages to human life. Purpose of this research is to find out impact value, hardness, macro defect, and micro structure as the result of holding time in molten Al-Si. Impact value of Al-Si due to molten holding time by variation of 0, 10,20, and 30 minutes are respectively 0.37 joule/mm2, 0.29 joule/mm2, 0.30 joule/mm2, and 0.26 joule/mm2. Meanwhile, hardness value of 0, 10, 20, and 30 minutes holding time are respectively 65.886 kg/mm2, 81.681 kg/mm2, 88.86 kg/mm2 and 86.265 kg/mm2. Brittle fracture occurred in all specimens and granule size of micro structure is smaller with the holding time. This research confirms that impact value has inverted correlation to hardness value. The lower of impact value, the higher hardness value. Based on micro structure observation on Al-Si casting due to molten holding time in 0, 10, 20, and 30 minutes variation, it is obtained smaller granule size.



Keywords

Al-Si; molten holding time; impact value; hardness value; macro defect; micro structure



Full Text: PDF



References


[1] Sudjana, H., “Teknik Pengecoran Logam Jilid 2 Untuk SMK.” Jakarta: Direktorat Pembinaan Sekolah Mengengah Kejuruan, Direktorat Jenderal Manajemen Pendidikan Dasar dan Menengah, Departemen Pendidikan Nasional, 2008.

[2] Azhari, A., “Pengaruh Proses Tempering dan Proses Pengerolan di Bawah dan di Atas Temperatur Rekristalisasi pada Baja Karbon Sedang Terhadap Kekerasan dan Ketangguhan Serta Struktur Mikro Untuk Mata Pisau Pemanen Sawit,” Jurnal e-Dinamis, Volume II, No.2 September 2012 ISSN 2338-1035, 2012.

[3] Suhardi, “Teknologi Mekanik III (Proses Pengecoran Logam).” Surakarta: UNS Pres, 1992.

[4] Surdia, T. & Saito, S., “Pengetahuan Bahan Teknik,” Jakarta: PT. Pradnya Paramita, 1999.

[5] Widarto, “Teknik Pemesinan Jilid 1 Untuk SMK.” Jakarta: Direktorat Pembinaan Sekolah Mengengah Kejuruan, Direktorat Jenderal Manajemen Pendidikan Dasar dan Menengah, Departemen Pendidikan Nasional, 2008.

[6] Surdia, T. & Chijiwa, K., “Teknik Pengecoran Logam.” Jakarta: PT Pradnya Paramita , 1980.

[7] Mondolfo, L.F., “Aluminium Alloys: Structure and Properties,” London: Butterworths, 1979.

[8] ASM International. “All Rights Reserved Aluminum-Silicon Casting Alloys: Atlas Microfractographs, 2004.

[9] Abidin, M.Z., “Identifikasi Fasa Intermetalik β-AlFeSi Pada Paduan Al-7wt%Si dab Al-11wt%Si yang Mengandung Besi.” Skripsi Universitas Indonesia, 2008.

[10] Bahtiar dkk. “Pengaruh Media Pendingin Minyak Pelumas SAE pada Proses Quenching dan Tempering Terhadap Ketangguhan Baja Karbon Rendah.” Jurnal Mekanikal. (online), 5 (1): 455-463, 2014.

[11] George E. D., “Mechanical Metallurgy,” Second Edition, Tokyo: Mc.Graw-Hill Kogakusha Ltd, 1988.

[12] Ismail. F. “Rancang Bagun Mesin Uji Impak Charpy.” Tugas Akhir Tidak diterbitkan. Semarang: Universitas Diponegoro, 2012.

[13] Hakim, H. A. “Pengaruh Temperatur Penuangan Terhadap Sifat Ketangguhan Impak (Impact Toughness) dan Kekerasan (Hardness) Aluminium Sekrap yang Ditambah Silikon 5%.” Skripsi Universitas Sumatera Utara, 2011.

[14] Puspitasari, D. “Perbedaan Ketangguhan dan Jenis Patahan Pada Duralium Akibat Proses Artifical Aging Dengan Variasi Media Pendingin Dromus Oil dan Air.” Skripsi Universitas Negeri Malang, 2015.

[15] Nurhadi, “Studi Karakteristik Material Piston dan Pengembangan Prototipe Piston Berbasis Limbah Piston Bekas.” Tesis Universitas Diponegoro Semarang, 2010.


Article View

Abstract views : 18 times | PDF files viewed : 9 times

Dimensions, PlumX, and Google Scholar Metrics

10.21070/r.e.m.v3i1.1590




Copyright (c) 2018 R.E.M. (Rekayasa Energi Manufaktur) Jurnal

Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.